This research includes the study of bending strength for the polymer composite materials. The first of all, the hand lay-up technology is used to prepare slates of the composite materials, epoxy resin was used as matrix for the reinforced materials that consist of artificial powders (aluminum oxide and copper) for reinforcing. The slates made of composite materials for both volume fractions 20% and 40% from the reinforced materials; all these slates were cut into samples with measurement (10x 100 mm) in order to carry out the bending strength test for samples by using cantilever bending test for both volume fractions 20% and 40%. The results and laboratory examinations for these samples shows increase in the bending strength and modulus of elasticity for composite materials when the volume fraction increase from 20% to 40% for reinforced materials, and these values decrease when the samples were immersion in distilled water for (30) days.
In recent decades, functionally graded porous structures have been utilized due to their light weight and excellent energy absorption. They have various applications in the aerospace, biomedical, and engineering fields. Therefore, the balance between material strength and light weight is the goal of the researchers to decrease the cost. Samples of PLA material were designed and manufactured using a 3D printer according to international standard specifications to study the effect of porosity gradient through thickness. An experimental three-point bending test was performed, and then simulations were performed using ANSYS 2022 R1 software on samples with functionally gradient different porosity layers to verify the experimental results. The results from the experiment and the numerical values were in excellent alignment with an error rate of no more than 13%. The maximum bending load and maximum deflection of the beam were specified experimentally and compared with the numerical solution. The maximum bending and the maximum deflection When the porosity layer in the middle of the beam, matched the ideal maximum bending load (190,194) N experimentally and numerically, respectively. The maximum deflection (5.9,6.4) mm experimentally and numerically, respectively was obtained in samples with varying porous layers.
The Cross-Rolling (CR) process is a severe plastic deformation technique that was used to roll aluminum alloy 6061. However, this process is accompanied by many disadvantages, such as spring back due to elastic recovery. This research aims to investigate the effect of cross-rolling on the spring back phenomenon by examining the main parameters that affect the forming process. Two different routes of cross-rolling were used: the first route, called two-step cross-rolling (TSCR), and the second, multi-step cross-rolling (MSCR), were employed to achieve high deformation and superior mechanical properties. The samples were bent using the V-bending process at three different speeds (5, 10, and 15 mm/min). The results showed that the rolling route and the change in cutting direction led to increased plastic deformation, thus increasing the spring-back factor. The type of route and cutting direction significantly impacted both the maximum load and the springback results.
This research paper is an attempt to reuse plastic waste fibre resulting from plastic sections industry as an additive to concrete matrix. The relationship between fibre volume fraction and mechanical properties of concrete and re-inforced concrete tiles was investigated. Three volume fractions of fibre ( 0.5 % , 1 % and 1.5 % - by volume of concrete ) were used through the experi-mental program. Tests’ results proved a slight decrease in concrete compres-sive strength as plastic fibre was added compared with the reference mix. Flexural behaviour of concrete tiles was enhanced as adding fibres. Adding fibre to Concrete results in a negligible reduction in concrete density. Fibre with high volume fractions improved Splitting tensile strength compared to the reference mix.