In General, original reactive powder concrete (RPC) consists of a superplasticized cement mixture with silica fumes, steel fiber and ground fine sand (150-600 ىm). The main purpose of the present work is to produce and study some mechanical properties of lightweight reactive powder concrete using a superplasticized cement mixture with high reactivity metakaolin (HRM) instead of silica fume, steel fiber (with different ratios ) with ground fine sand (150-600 ىm) and light weight material called (Perlite ) also with different ratios .This investigation was carried out using several tests, these tests were compressive strength, modulus of rupture, modulus of elasticity, density and absorption, and performed for specimens at ages of 3, 7, 28 days, respectively. The tests results were compared with a reference mix. The experimental results shows that , with different ages, (for constant Perlit ratio for 0% to 10% as additional cementtitious materials) addition of 1% steel fiber will improve about (8.3%-10% , 3.2%-11%and 0.25%- 8%) for compressive strength , modulus of rupture, and modulus of elasticity respectively, and increase density, absorption about (0.8%-1.8%,4.5%-8.2%) respectively. Also an increase of steel fiber ratio to 2% will improve about (16.5%-20.3%, 9.0%-17%, and 1.7%-11.5%) for compressive strength , modulus of rupture and modulus of elasticity respectively, and increase density, absorption about (1.7%-2.3% , 7.3%-8.3%) respectively. For same steel fiber ratio about 0% to 2%, increasing Perlite ratio to 2.5% will decrease about (17.3%-18.8%, 9.5%-15.5%, 4.4%-16.6%, and 4.98% - 6.9%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption to about (55.5% - 66.5%). Increasing the ratio to 5% will also make a decrease of about (36%-36.77%, 33.7%-37%, 16.5%- 21.88%and 15.91%-19.74%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption for about (106%- 110.5%) . Increasing the ratio to 10% will also decrease about (45.98%-47.2%, 46.5-54.2%, 30.6%- 35.57%and 19.4%-23.36%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption about(183%- 192.6%). To produce structural lightweight concrete, the tests results show that the optimum steel fiber is 1% by volume and optimum Perlite ratio is 2.5% by weight of cement as additional materials.
Recently, many attempts were made to use steel fiber reinforcement to improve some soil properties. In this research, the effect of steel fibers on the compaction and mechanical properties of cement stabilized soil (silty soil) was studied. Variables such as stabilizer (cement) content, amount and type of steel fibers were studied. Results indicate that the addition of fibers leads to increase in the maximum dry unit weight. On the other hand, a maximum value of unconfined and tensile strength were obtained with the addition of 0.5 % short fiber (FS) and 1.5 % long fiber (FL) respectively.
The aim of this paper is to study experimentally the effect of steel fibers content on the modulus of elasticity of High Performance concrete HPC in different curing age. The results showed that adding steel fibers to HPC led to a considerable improvement in static and dynamic modulus of elasticity where at 90 day water curing the percentages of increasing in static modulus of elasticity of High Performance Steel Fiber Concrete HPSFC relative to HPC were 8.2%, 9.98%, and 11.88% at 0.5%, 1%, and 1.5% steel fibers by total concrete volume, respectively. While, the improvement of dynamic modulus of elasticity of HPSFC relative to HPC at 28 day were 8.09%, 10.7%, and 11.07% % at 0.5 %, 1 %, and 1.5 % respectively.