Previous studies showed that fire incidents cause a considerable deterioration of limestone samples' engineering and physical properties. Various laboratory tests were used in previous studies to investigate the properties of limestone. These tests included destructive and non-destructive tests like the hammer test, ultrasonic pulse velocity test, water-capillary rise test, and water transfer properties test, as well as destructive tests like the unconfined compression test and Brazilian tensile test. The stones of buildings exposed to fire are occasionally assessed on the site. This study analysed the physical and mechanical changes that occurred to the limestone samples when subjected to high temperatures, the damage mechanism, and laboratory or field damage assessment. This study also includes a review of the most significant studies that looked at how alternative cooling techniques—rapid water cooling or gradual air cooling—affect stone samples subjected to high temperatures and compared the behaviour of the samples in each scenario
The white cement Kiln dust (WCKD) is a secondary production from the cement industry through its production operation. Environmentally, it is considered as an unwanted waste because it causes air pollution and ground congealment, and it is needed great efforts and financial support to disposal it. In this study, the WCKD was used partially instead of limestone as a filler in the asphalt mix, where it was used by ratios of 0%,25%,50%,75% and 100% from the weight of limestone. An evaluation of the mechanical characteristics was conducted by carrying out Marshall test and Indirect Tensile test, and the results showed that the increase in the WCKD percent reduces the asphalt mix density and increases the percentage of air voids, while the other characteristics (stability, Marshall Stiffness, flow and Indirect Tensile Strength) increase when the WCKD ratio is 25% and 50%. These those characteristics start decreasing when the WCKD ratio was 75% and 100%. The study showed that the optimum ratio of the WCKD is 50% from the limestone weight, and the WCKD cannot be used as a filler entirely in asphalt mix, but it can be used partially.
The White Cement Kiln Dust (WCKD) is a byproduct material, formed in cement factory during the operation of cement production. In highway construction, the WCKD can be used in different ways such as stabilizing the subgrade of highway embankment and as mineral filler in Hot Mix Asphalt (HMA); the latter usage will give clean and healthy environment in addition to more economy. In Iraq, there are two common types of fillers, Portland cement and lime stone powder. In this research, WCKD taken from Fallujah cement plant used as mineral filler in addition to two common types. Various percentages , such as 100%WCKD, 50%WCKD + 50%Cement(C) ,100%C , 50%WCKD+50%Limestone (L), and 100% L, were used to prepare asphaltic concrete mixes. In general, five tests were used to evaluate the performance of these mixes. Standard Marshall Test procedure was applied under three different conditions, two of them at two temperatures at 60 OC and 70 OC and in the third one it was used to test samples immersed in water, at room temperature(24 OC), for four days. Indirect Tensile Strength Test (ITST) was used to evaluate conditioning and un-conditioning samples. All test results, when compared with controlled asphalt concrete sample (Sample contained 100% limestone as filler), were acceptable and within the AASHTO and Iraqi Standard Specifications of Roads & Bridges 2003. Stability values, at standard condition test, of samples containing 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L are 11.9kN, 13.2kN, and 14.0kN respectively, while for controlled sample was 9.0kN. The Marshall stiffness values showed similar trends, for samples having 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L giving 3.22kN/mm, 3.38kN/mm, 3.5kN/mm respectively but for controlled sample was 2.43 kN/mm. Same trends of results gained in ITST .The results showed the beneficial using of WCKD as filler that will conserve the environment and encourage the HMA producers to use this inexpensive material in their works.
The study of springs Abu-Aljeer natural asphalt at proven of al-anbar (Iraq), to find a mean of exploiting the asphalt springs as alternative energy resource, Included two stages The first: Separation the components of asphalt in two ways the first is column chromatography and second represented by extraction- chromatography. The results of separation were 10.20% Asphltene, 89.18% Maltene which separated lately to (Paraffinic 45.23%, Aromatic 28. 39% and Resin 21.66%). The second: Trying to improve the asphalt specifications by using natural materials that are available locally (limestone) with (5, 15, 25, 35%), which have given good results. Rheological properties have been tested, in such average that (virgin Softening was 430C, became 560C, Penetration was 110 dropped 39 and viscosity was 11355 turnedy other 47231cent-Stok, mm2Sec), and flash point ( 1790 C became 200 0C), Fractionated parts of asphalt were characterized by (UV), (FT-IR) spectra. This study also clarified paraffin compounds which represent the main part material and the colloidal state is in Gel phase.